Filter elements for gas or liquid

ABSTRACT

A self-supporting tubular fibrous filter element consists of elongated fibers compacted in a direction parallel to the central axis of said tubular element to have a substantially constant density throughout the length and thickness of the tube with a majority of the fibers in parallel to one another in a circumferential direction about the said axis. When required, a perforated cylindrical support sheet is molded into at least one cylindrical face of the element.

This is a division of application Ser. No. 3,450, filed Jan. 15, 1979 now U.S. Pat. No. 4,303,472.

This invention relates to filter elements.

In U.S. Pat. No. 4,111,815 there is described a method of forming a filter element which comprises dispersing a mass of fibres in a liquid to form a slurry, draining the liquid through a filter surface on which the fibres collect while an apertured sheet of supporting material is located at a selected distance above the filter surface, so that the fibres build up from the filter surface through the apertures in the supporting material to a predetermined distance above the supporting material, removing the collected fibres containing the sheet of supporting material from the filter surface, and bonding the fibres to one another and to the supporting material by means of a synthetic resin.

One aspect of the present invention is based on further experiments that demonstrate unexpectedly satisfactory results if, in the aforesaid method, the sheet of supporting material is omitted or, if provided, is located substantially in contact with the filter surface so that the sheet of supporting material becomes moulded into one surface of the filter element. The invention results in the production of a particularly efficient fibrous filter that is very economical to manufacture.

According to the present invention, a method of forming a tubular filter element comprises dispersing a mass of fibres in a liquid to form a slurry, applying the dispersion under pressure to a filter surface so that the fibres collect as a layer covering the filter surface while the liquid passes through the filter surface, the fibres being compacted progressively in a direction parallel to the central axis of said tubular element fron one end to the other end of said element during the fabrication of said tubular element, and bonding the fibres in the collected mass of fibres, after drying, to one another by means of a synthetic resin. A sheet of material that is to provide a support for the filter element may be mounted in contact with at least a portion of the filter surface so that the support sheet becomes moulded into one surface of the collected mass of fibres. Thus, when the support sheet, which may be provided by very fine mesh material, is removed, the fibres are found to have penetrated through the support sheet leaving their outer surface flush with the outer surface of the support sheet, which may be a layer of expanded metal. In the past, in the case of cylindrical filter elements, these have required the addition of a separate support sheet to give strength, but the present moulding method enables the filter cylinder and support sheet to be produced as an integral part in one operation with precision, saving time and labor.

In general, it is desirable to make the apertures and open area of the support sheet as large as possible. However, it is difficult to specify the largest aperture that can be used. The smallest aperture at present contemplated is 0.25 mm diameter. However, it must be remembered that certain fibres, such a potassium polytitanate, e.g., potassium dititanate, have a diameter of 0.5 microns and length of up to 0.15 mm and these can penetrate apertures of 0.25 mm and smaller.

In the case of the filter surface, expanded metal with narrow flat strips between overlapping elongated apertures, an aperture size of 0.75 mm by 0.5 mm has been found to be practical. This gives a good surface finish. An aperture size of 1 mm by 0.75 mm will of course give a somewhat rougher finish.

Other practical examples or rigid supports have had apertures of 2.8 mm of 0.8 mm providing an open area of 26% of the area of the support sheet, and 43 mm by 20 mm with an open area of 83%. In general it has been found that the support sheet results in a very small flow restriction, of the order of 1% to 2% of the total flow.

In a modification of the aforesaid method, the support sheet consists of a rigid foam or sintered material thereby eliminating the necessity for the use of the very fine mesh material in the production of the filter element.

When, as in the aforesaid prior U.S. Pat. No. 4,111,815, the binder is used not only to bond the fibres together but also to the support sheet, this may be, for example, silicone, polyurethane, expoxy or phenolic resin. Heat cured resins are preferred though air drying resins can be used. The weight of the resin binder depends on the strength required. Generally the weight of the binder is no more than 100% of the weight of the fibres.

It has been found that the use of pressure in the method according to the invention results in a progressive compacting of the fibres as the filter element is built up, with a majority of the fibres being disposed so that they are directed, in some measure, approximately in parallel with one another. This gives particularly advantageous results, whether or not a support sheet is used. According to a further aspect of the invention, therefore, a filter element comprises a mass of fibres compacted together and bonded to one another with a synthetic resin, a majority of the fibres being disposed so that they are directed, in some measure, approximately in parallel with one another.

In order that the invention may be clearly understood and readily carried into effect, examples of the invention will now be described with reference to the accompanying drawings, in which:

FIG. 1 is a sectional elevation of part of a filter element;

FIG. 2 is an enlargement of a portion of FIG. 1;

FIG. 3 is a sectional elevation of part of another filter element;

FIG. 4 is a diagram showing apparatus for manufacturing a filter element;

FIG. 5 is a sectional elevation of a detail of the apparatus of FIG. 4;

FIG. 6 is similar to FIG. 5 but relates to a different phase in the operation of the apparatus;

FIG. 7 is a sectional elevation of a further filter element; and

FIGS. 8 to 18 show portions of various sealing arrangements for the ends of filter elements.

The portion of the filter element shown in FIGS . 1 and 2 may be part of the wall of a cylindrical filter element although it can equally well be regarded as part of a disc, sheet or conical or frusto conical cylindrical shape (for example closed at one end as shown in FIG. 7). A similar method may also be used for the production of concave or convex discs. The bulk 1 of the filter element comprises fibre material; for example, glass, ceramic, synthetic fibres, asbestos, mineral wool, organic or silicate fibres. Raw borosicicate microfibre is a preferred material. For cartridge type filters to be used in liquid filtration, cellulose, wool, synthetic polymer (e.g. polypropylene and acrylic) fibres, and combinations of these, also such combinations containing a portion of borosilicate microfibre, can very advantageously be used. These combinations can also be used for gas filtration. Both faces of the fibre mass 1 have an apertured support sheet 2 moulded thereto so that the fibrous mass penetrates through the apertures in the sheets to present surfaces that are flush with the outer surfaces of the sheets (FIG. 2). Each support sheet consists of an apertured or open pore rigid material such as a perforated, expanded or woven material which, in turn, may be of metal, plastics, glass or ceramic. Expanded metal is a preferred material. The total area of the openings in the support sheets depends on the use to which the filter element is to be used.

The filter element of FIG. 3 is similar to that of FIG. 2, but only one support sheet 2 is used. Where one support sheet is used, this is generally located on the downstream side of the fibres. This not only gives strength where it is required but does not reduce the inlet surface area of the filter, thereby increasing the dirt holding capacity. For low pressure use as for example in vacuum systems, the support sheet can be of comparatively light construction but, when used in a high pressure system, either with gas or liquid, the support sheet can be of heavier construction.

In a further example, no support sheet is used. This example consists of a tube made from raw borosilicate microfibre moulded by pressure forming into the cylindrical shape by a method as described below with reference to FIGS. 4 to 6. The moulded tube is then dipped into a solution of resin in a solvent so as to impregnate the fibrous material and is then heat cured. By using a method as described below a filter element without any support sheet can be constructed with very advantageous properties. For example such filter elements 54 mm long, 44 mm outside diameter and 34 mm inside diameter have been constructed and tested to give the following characteristics:

    ______________________________________                                         D.O.P.   BURST    FLOW     Δp                                                                             p    O.D.T.                                   %        bar      NM.sup.3 /H                                                                             bar   bar  % w/w                                    ______________________________________                                         >>99.999 >7.0     45       .069  7.0  15.0                                     99.97    >7.0     45       .069  3.0  27.0                                     99.90    >7.0     48       .035  3.0  25.0                                     99.80    >7.0     52       .035  3.0  21.0                                     99.80    >7.0     50       .035  4.0  35.0                                     ______________________________________                                    

In the above table p is the operating test pressure, Δp is the pressure loss across the filter and O.D.T. is the ratio of the oven dried total weight of resin to the fibre content of the filter element. The binder used in all the filter elements represented in the above table was a silicone resin, which is preferred, but many other binders can be used to give comparative test results. The highest resin content which is in the last tabulated example, is 35% but this can be raised to as high as 100% while still providing satisfactory characteristics. However, 25% has been found admirably satisfactory for most applications.

The effect on performance of varying the wall thickness of an unsupported tubular filter element is shown in the following table relating to a larger element 200 mm long, 66 mm outside diamenter and 54 mm inside diameter for sample (a) but 46 mm inside diameter for sample (b):

    ______________________________________                                                 D.O.P.   FLOW     Δp                                                                              p    O.D.T.                                   SAMPLE  %        NM.sup.3 /H                                                                             bar    bar  % w/w                                    ______________________________________                                         (a)     99.99    306      .017   4.2  16.0                                     (b)     99.999   170      .017   4.2  16.0                                     ______________________________________                                    

In the above table the pressures p is a gauge pressure above atmospheric pressure while Δp, of course, is a pressure differential.

The above table shows that it is effectively only the flow capacity and efficiency that is affected by the increase in wall thickness. In practice, it is thought that about 3 mm will prove to be a lower limit for the wall thickness.

The good results, exemplified by the above tables, are believed to arise from the packing pattern of the fibres that arise as a result of a method of manufacture such as described below with reference to FIGS. 4 to 6. This method of manufacture results in the fibres lying more uniformly in a circumferential direction around the tubular filter element, than is possible with known vacuum methods which display a totally random packing pattern. The more regular packing in the filter elements of the invention does not detract from their efficiency.

Although the filter elements described immediately above have no rigid support sheet, they can be provided with an inner, outer, or both inner and outer layer of woven or non-woven flexible material to improve the handling characteristics. Such a layer can be incorporated during the manufacture of the filter element by a method as described below. The fibres would generally penetrate through an aperture or pore structure of the flexible material. Moreover in the case of a filter element with a single rigid support sheet as shown in FIG. 3, the opposite face of the fibrous structure can be provided with a layer of flexible material.

Simple, unsupported tubular filter elements as described above may be formed with a variety of surface patterns, for example circumferential or longitudinal grooves, to increase the surface area.

FIG. 4 shows diagrammatically apparatus for forming a tubular filter element. When this apparatus is in operation, water and borosilicate microfibres are fed into a blending tank 31. Hydrochloric or sulphuric acid is added until the pH value reaches 2.8 to 3.5. Borosilicate microfibres are found to disperse more readily at this value. It has also been found that the fibres disperse more readily if the solution temperature is increased to about 35° C. The quality of the fibres that are used depends on the grade of the filter element that is to be used. The fibre to water ratio (by weight) is generally 0.05% but can vary between 0.01% and 0.5%. A binder such as colloidal silica may be introduced into the slurry at this stage. It has been found advantageous to use this type of binder to impart additional strength prior to resin impregnation. The final dispersion is effected by a mechanical agitator 32 and takes about 15 minutes.

With valves 33 and 34 closed and valve 35 open, a pump 36 transfers the dispersion to a pressure vessel 37. The precise quantity transferred depends on the fibre/water ratio and the size of the filter element to be produced.

Next the valve 35 is closed and the valve 33 is opened to admit compressed air to the pressure vessel 37. Generally the pressure used is 3.5 bar. This top pressure is the forming pressure and can be varied according to the efficiency required. The efficiency can be varied within a range, e.g., 99.9% to 99.999%, using the same fibre blend. The forming pressure may be as low as 0.3 bar, but a pressure of 3.5 bar has been found highly satisfactory with the fibre blend adjusted to suit the required efficiency.

The next step is to open the valve 34 to enable the dispersion to flow into a moulding rig 38 shown in detail in FIGS. 5 and 6. The moulding rig includes inner and outer vertical cylinders 39, 40 defining a space 41 through which the dispersion can flow into a cylindrical moulding space 42 defined between a fine mesh screen 44, supported by a machined perforated cylinder 45, and a core 43 when in the position of FIG. 5. FIGS. 5 and 6 show the filter element being molded as a unit with an outer rigid cylindrical support sheet 2, but it will be appreciated that for a simple borosilicate microfibre filter tube, this can be omitted. Alternatively, of course, an inner support sheet can be moulded into the inside surface of the tube, either instead of or as an addition to the outer sheet 2. The bottom of the moulding space is covered by a fine mesh screen 46. A reciprocable sleeve 47 is mounted to slide outside the cylinder 40 and perforated cylinder 45.

With the core 43 and sleeve 47 in the positions shown in FIG. 5, the water drains away through the screen 46 and lower end of the screen 44 into a tank 48 (FIG. 4) while the mass of fibres begin to build up progressively in the moulding space 42. After all the fibres have accummulated in the molding space, the air pressure is maintained so as to remove residual water from the fibres and so dry the formed filter. The valve 34 is then closed. During the molding process, a pump 49 continuously pumps the water from the tank 48 to a holding tank 50 from which the water is recycled.

Finally the core 43 is removed to enable the formed filter element to be removed from the rig 38. The process can then be started once more. As an example, it has been found that the time taken to mold a tubular filter element 250 mm long, 65 mm outside diameter with a wall thickness of 10 mm takes approximately one minute. The formed filter element is removed to a hot air dryer for final drying and is then resin impregnated and oven cured to harden the resin.

Particularly in the case of long filter elements, e.g., over 50 mm, it has been found desirable progressively to raise the sleeve 47, substantially at the same rate that the height of the fibre mass increases, in order to maintain an uninterrupted flow of the dispersion to the point where the mass of fibres is building up. The movement of the sleeve 47 then terminates as shown in FIG. 6.

The core 43 is formed with an upper portion 51 of reduced diameter. This is to enable an additional internal layer of fibrous filter material to be added to the filter material formed in the molding space 42, by feeding a further dispersion through the cylinder 39 into a molding space 52 (FIG. 6) between the molding space 42 and the core portion 51 when the core 43 is lowered. The water from the new layer escapes through the fibres in the space 42. The new layer may be of higher or lower efficiency than the tubular element formed in the space 42. This arrangement enables a filter element of graded density to be produced as part of an integral process.

Investigations have shown that the fibres in a finished filter element produced by the method described above with reference to FIGS. 4 to 6 are predominantly layered in planes perpendicular to the direction in which the dispersion flows into the molding space. It has further been found that the same packing pattern arises throughout the range of forming pressures that can be used effectively in practice. Advantages of this packing pattern appear from the results tabulated above.

For some applications of the invention, where cellulose fibres or combinations of cellulose fibres with borosilicate fibres are used, a melamine or phenolic resin binder may advantageously be used for the bonding material. Cellulose when bonded with melamine resin is approved as being suitable for potable water and sanitary conditions. Phenolic resin is preferred for higher temperature work. The combination of cellulose fibres with other fibres provides economies both in regard to cost and production time, good flow characteristics and chemical resistance, and controlled selection of pore size by blending different fibre materials with cellulose. It has been found that by blending 20% borosilicate microfibre with 80% cellulose by weight the production time for the filter can be reduced by 30%. In this case when the fluid is water the pressure drop (Δp) across the filter was 0.15 bar with a flow rate of 16 liters per minute. With a weight to weight ratio of 50%, Δp was found to be 0.15 bar with a flow rate of 22 liters per minute. The glass fibre size (diameter) was 3.8 to 5.1 microns and the cellulose a bleached softwood kraft. The bonding material, e.g. melamine resin, phenolic resin or other synthetic resin, can be applied in one of three different ways. Firstly, by forming a mass of fibres in a molding rig such as shown in FIGS. 5 and 6, then impregnating the mass after drying by dipping in a resin solution and curing the resin in an oven. Secondly, by preparing the cellulose fibre and separately mixing the borosilicate fibre with a resin solution, bringing the two mixtures together, forming the mass under pressure in the molding rig and curing the mass. Thirdly, all the fibres and resin solution can be mixed in a single tank, passed to the molding rig, the mass being subsequently cured.

A cylindrical filter element for liquid filtration having a combination of fibres as described above may have an outside diameter of 64 mm, a wall thickness of 18 mm and various lengths, such as 250 mm. No support sheet is necessary for many uses but can be added when necessary. The filter is preferably arranged for flow from outside to inside the cylinder to give greater surface area for collection of dirt. This area can be increased by forming longitudinal or circumferential grooves in the outside surface of the cylinder.

Instead of using a compressed gas to apply pressure to the slurry in the molding rig, a hydraulic pump may be used, this pump being arranged to withdraw the slurry from the blending tank and force it into the molding rig.

Tubular or cylindrical filter elements made in accordance with the invention may be mounted in a variety of filters, in particular those shown in FIGS. 5, 6, 7 and 13 in the aforesaid prior U.S. Pat. No. 4,111,815. As in that prior patent also the ends of the cylindrical filter elements may be fitted into end caps in a variety of ways. Such ways are shown in FIGS. 8 to 17 of the present specification.

FIGS. 3 to 13 show cases where the end of a cylindrical, unsupported filter element 10 is fitted into an end cap 11 using a gasket seal 12 (FIG. 8), a double taper seal 13 (FIG. 9), an outside taper seal 14 (FIG. 10) an inside taper seal 15 (FIGS. 11 and 12) and a double taper flange seal 16 (FIG. 13). For a cylindrical filter element with an inside support sheet 17 an outside taper seal 14 (FIG. 14) may be used. For an outside support sheet 18 (FIG. 15) an inside taper seal 15, or a single taper flange seal 19 (FIG. 16) may be used. In the case of a filter element having inside and outside support sheets 20, 21 (FIG. 17) a gasket seal 12 (FIG. 17) can be used. In all forms of the filter element constructed according to the invention, an open pore filter layer 22 or sleeve, as shown in FIGS. 12 and 17, can be used if required to act as a pre-filter or as an after-filter to drain coalesced liquids. This layer or sleeve can be an open pore plastic or metal foam or a layer or layers of non-woven material such as felt. As a further alternative the filter element can be dip sealed into end caps as shown in FIG. 6 of the aforesaid prior patent. FIG. 18 shows an arrangement similar to FIG. 15 with an internal supporting spring 24 in place of any inside support sheet.

Filters made in accordance with the invention can be used for either gas or liquid filtration. The efficiency can be as high as 99.99998% when tested to DS 4400 or can be produced with a micron rating in various stages between 1 and 50 microns. A further method of increasing the efficiency of the moulded filter material is by compressing the material while being resin impregnated and cured.

A further material that can be used for the support sheet is a rigid metal foam. The fibres can be moulded directly onto such foam so that they penetrate only so far into the thickness of the foam sheet, but the fine mesh screen 44 can be eliminated in this process because the foam sheet itself provides the filter surface through which the water is drained. The same method can be used in the case of the aforesaid sintered support sheet. The same method can also be used with foam consisting of plastics material, which may be flexible or semi-rigid. However, very advantageously a rigid polyvinyl chloride coated plastic foam can be used.

Among the many possible uses of the filter according to the invention are the removal of oil from compressed air, pre-filtration, aeration, vacuum filtration, liquid filtration, air sterilization and for pneumatic silencing. 

We claim:
 1. A fibrous filter element comprising a tubular wall consisting of a mass of elongated fibers compacted at substantially constant density throughout the length and thickness of the said tubular wall as a result of said fibers having been compacted progressively in a direction parallel to the central axis of said tubular wall from one end to the other end of said tubular wall during the fabrication of said tubular wall, a majority of said elongated fibers being oriented approximately in parallel to one another in a circumferential direction about the central axis of said tubular wall, a synthetic resin bonding said fibers together, and a tubular sheet of apertured material disposed external of said tubular wall adjacent the outer face of said tubular wall for providing additional support for said bonded mass of circumferentially oriented fibers, the outer face of said tubular wall being joined to said sheet with some of said fibers penetrating through the apertures in said sheet and filling said apertures to present fiber surfaces substantially flush with the surface of said sheet remote from said wall.
 2. A filter element according to claim 1, including an additional tubular support sheet of apertured material disposed adjacent the inner face of said tubular wall. 